Solid-State Oxide Slurry

LATP water-based slurry, D50 0.30 um

Water-based LATP slurry with fine particle size for separator coating studies.

Product Details

LATP slurry

Water-based LATP slurry with fine particle size for separator coating studies.

Category
Solid-State Oxide Slurry
Availability
RFQ

Typical Specification

  • Particle size: D50 0.30 +/- 0.05 um
  • Solid content: target +/- process range
  • Viscosity: <= 80 mPa.s
  • pH: 5-9
Request QuoteBack to Solid-State Materials

Final values should be confirmed by grade, lot, COA/TDS, and intended processing conditions.

Technical Selection Guide

How should LATP water-based slurry, D50 0.30 um be selected and tested?

LATP water-based slurry, D50 0.30 um is a process-ready oxide-electrolyte dispersion for coating, separator-layer, and composite-electrolyte development. Slurry performance depends not only on LATP particle size but also on solids content, carrier compatibility, dispersion stability, rheology, drying, binder selection, and the final coated-layer density.

Why developers evaluate it

  • Coating and separator-layer process development
  • Composite cathode or polymer-ceramic studies
  • Pilot mixing, drying, and lamination trials

Development considerations

  • Confirm carrier and binder compatibility
  • Control sedimentation, viscosity, and coating uniformity
  • Measure conductivity after drying and densification

How to compare it

Compare slurry grades by coated-layer performance rather than liquid appearance alone. Relevant listed parameters include Particle size: D50 0.30 +/- 0.05 um; Solid content: target +/- process range; Viscosity: <= 80 mPa.s. Confirm the final solids content and processing window for the intended coating method.

Solid-State Electrolytes Solid-State Materials Guide Compare Electrolyte Families Powder Screening Guide

Characterization

Tabular Data & Supporting Images

ParameterSpecification / ResultMethod
AppearanceWhite slurry, uniform colorVisual inspection
D50 particle size0.30 +/- 0.05 umLaser particle-size analyzer
Solid contentTarget value -0.5% to +1.5%; typical range 20-40%Solid-content test
Viscosity<= 80 mPa.sViscometer
pH5-9pH meter
Magnetic impurities<= 500 ppbICP-OES
Use caseLithium-ion battery separator coatingApplication guidance